Ingeo? 4032D
聚乳酸
NatureWorks? LLC
产品说明：
Ingeo 4032D can be converted into a biaxially oriented film with use temperatures up to 300°F (150°C). This film has excellent optics, good machinability and excellent twist and deadfold. These properties make 4032D film an ideal product for laminations and other packaging applications. Additional properties include barrier to flavor and grease and oil resistance.
| 基本信息 |
|
|---|
| 特性 | 光学性能 可更新资源 可切削 耐油性能 耐油脂性能 生物可降解 弯折及捻度持久性
|
| 用途 | Bi-axially Oriented Film 包装 层压板
|
| 机构评级 | FDA 食品接触, 未评级 欧洲 10/1/2011 12:00:00 AM
|
| 形式 | |
| 加工方法 | |
Ingeo? 4032D 物性表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 1.24 | g/cm? | ASTM D1505 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 薄膜厚度 - 经测试 | 25 | ?m |
|
| 割线模量 |
|
| ASTM D882 |
| MD : 25 ?m | 3450 | MPa | ASTM D882 |
| TD : 25 ?m | 3790 | MPa | ASTM D882 |
| 抗张强度 |
|
| ASTM D882 |
| MD : 屈服, 25 ?m | 103 | MPa | ASTM D882 |
| TD : 屈服, 25 ?m | 145 | MPa | ASTM D882 |
| 伸长率 |
|
| ASTM D882 |
| MD : 断裂, 25 ?m | 180 | % | ASTM D882 |
| TD : 断裂, 25 ?m | 100 | % | ASTM D882 |
| 埃尔曼多夫抗撕强度 |
|
| ASTM D1922 |
| MD : 25 ?m | 17 | g | ASTM D1922 |
| TD : 25 ?m | 14 | g | ASTM D1922 |
| 二氧化碳传输速率 | 2850 | cm?/m?/24 hr | 内部方法 |
| 透氧率 | 675 | cm?/m?/24 hr | ASTM D1434 |
| 水气透过率 | 380 | g·mm/m?/atm/24 hr | ASTM F1249 |
| Spencer Impact | 2.50 | J |
|
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 结晶峰温度 (DSC) | 155 到 170 | °C | ASTM D3418 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 光泽度 (20°, 25.4 ?m) | 90 |
| ASTM D2457 |
| 雾度 (25.4 ?m) | 2.1 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 79.4 | °C |
|
| 干燥时间 | 4.0 | hr |
|
| 建议的水分含量 | 0.025 | % |
|
| 料筒1区温度 | 179 | °C |
|
| 料筒2区温度 | 191 | °C |
|
| 料筒3区温度 | 199 | °C |
|
| 接头温度 | 199 | °C |
|
| 熔体温度 | 202 到 218 | °C |
|
| 口模温度 | 199 | °C |
|
| 挤压说明 |
|---|
| Screw Speed 20-100 rpm |